HY115 high-temperature repair agent

nine hundred
Product information:
  HY115 high-temperature repair agent can be widely used for filling casting defects, grinding repair and sealing of iron parts. Repair of steam and hot oil pipelines, engine cylinder blocks, wear resistance, corrosion, and scratches. Repair of paper drying cylinders and plastic molding molds. HY115 high-temperature repair agent has wear resistance, corrosion resistance, and aging resistance. After repairing with HY115 high-temperature repair agent, the color can remain consistent with the substrate being repaired. HY115 high-temperature repair agent is easy to use and can be used for various mechanical processing such as turning, milling, drilling, and grinding after curing. Used for filling casting defects and repairing and regenerating metal parts for wear, corrosion, and scratches.
Product performance:
nine hundred and one
usage method:
1. Surface treatment: Polish and roughen the surface to be repaired to a depth of at least 1mm, and then clean it with HY115 cleaning agent or acetone. The surface to be repaired must be clean, free of water and oil stains
2. Mixing: Weigh components A and B according to the specified weight ratio, mix thoroughly, and make the color completely consistent
3. Coating: Use a glue knife to apply the pre mixed repair agent to the surface to be repaired. Apply a small amount first, press repeatedly with the glue knife, fully soak, and then apply the remaining repair agent, leaving enough space for processing
4. Curing: After curing at room temperature for 12 hours, various mechanical processing can be carried out. When the ambient temperature is below 15 ℃, the curing time can be appropriately extended. 80° Holding at ℃ for 3 hours can not only shorten the curing time, but also achieve better coating performance.